Название: Exploration of the viscosity temperature dependences and microstructure of magnesium-based commercial alloy AZ91D with small additions of calcium
Авторы: Abaturov, I. S.
Popel, P. S.
Brodova, I. G.
Astafiev, V. V.
Peijie, Li
Дата публикации: 2008
Издатель: IOP PUBLISHING LTD
Библиографическое описание: Exploration of the viscosity temperature dependences and microstructure of magnesium-based commercial alloy AZ91D with small additions of calcium / I. S. Abaturov, P. S. Popel, I. G. Brodova [и др.] // 13th international conference on liquid and amorphous metals. — 2008. — Vol. 98.
Аннотация: The technique of rotating oscillation damping of a crucible filled in with the melt under investigation was used for measurement of viscosity of the Mg-based AZ91D commercial alloy with various additions of calcium. The viscosity was measured in liquid state in temperature interval from 600 up to 840 degrees C. The comparative metallographic investigation of the structure of samples with calcium content of 0.0, 0.4, 0.6 and 0.8 wt.% which were crystallized just after re-melting at the temperature of 640 degrees C and after heating in liquid state up to 850 degrees C were made. It was shown that the thermal treatment of samples in liquid state is accompanied by considerable changes in the cast structure that forms after the crystallization of the samples.
URI: http://elar.uspu.ru/handle/uspu/5367
Конференция/семинар: 13th Conference on Liquid and Amorphous Metals
Дата конференции/семинара: JUL 08-14, 2007
DOI: 10.1088/1742-6596/98/6/062023
Располагается в коллекциях:Научные публикации, проиндексированные в Scopus и Web of Science

Файлы этого ресурса:
Нет файлов, ассоциированных с этим ресурсом.


Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.