Название: Effect of Homogenizing Heat Treatment of Liquid Aluminum-Copper Alloys on the Structure of Rapidly Crystallized Specimens
Авторы: Astaf'ev, V. V.
Kurochkin, A. R.
Yablonskikh, T. I.
Brodova, I. G.
Popel', P. S.
Дата публикации: 2017
Аннотация: Centrifugal casting into a massive slot chill mold was used to prepare two series of specimens of alloys of the Al - Cu system, containing from 10 to 32.2 at.% Cu. The first series was fabricated without a homogenizing heat treatment of the melt, while the second series was fabricated with heating of the melt to 1400A degrees C. Both kinds of specimens were cast at the same temperature in order to provide for the same cooling rate of about 10(4) K/sec. The structures, phase compositions and microhardnesses of the structural components are compared. It is established that the homogenizing heat treatment changes the kinetics of crystallization and, hence, the proportion of phases in the alloy structure and the copper content in them.
Ключевые слова: ALLOYS OF ALUMINUM - COPPER SYSTEM
HOMOGENIZING OF MELT
RAPID QUENCHING
STRUCTURE OF ALLOY
AL-SI ALLOYS
URI: http://elar.uspu.ru/handle/uspu/6667
DOI: 10.1007/s11041-017-0177-y
Располагается в коллекциях:Научные публикации, проиндексированные в Scopus и Web of Science

Файлы этого ресурса:
Нет файлов, ассоциированных с этим ресурсом.


Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.